Pengaruh Kadar Perekat Terhadap Karakteristik Briket Arang Limbah Kayu Karet (Hevea brasiliensis Muell. Arg)
DOI:
https://doi.org/10.23960/jtep-l.v10i3.283-295Abstract
The study aimed to determine the effects of adhesive content on rubber wood charcoal briquette characteristics. Wood charcoal was produced using a double-drum retort kiln at > 500°C. Wood charcoals were crushed into powder and then mixed with tapioca adhesive of 5%, 10%, and 15%. The charcoal-adhesive mix was then pressed using a hydraulic press machine. For comparison, rubber wood biomass briquettes were also produced using wood particle-adhesive mix with similar adhesive content. Biomass and charcoal briquettes characteristics as physical properties (density and water absorption), chemical properties (ultimate analysis, and FTIR analysis) and energy properties (calorific value) were evaluated. The results showed that density ranged between 0.52-0.56 g/cm3, water absorption of 6.54-7.47%, C content of 82.67-84.41%, H content of 3.28-3.60%, N content of 0.67%-0.74%, and calorific value of 30.76-32.86 MJ/kg. The results of FTIR analysis showed changes in the spectrum of the wave band on the functional groups OH, CH, CH, C=C, and C=O, indicating the decomposition of the chemical components of rubber wood due to pyrolysis. The results prove that increasing the adhesive content can reduce the quality of briquettes. Based on physical, chemical, and energy properties, charcoal briquettes with 5% adhesive showed better characteristics than briquettes with 10% and 15% adhesive content, showing water absorption of 6.54%, C content of 84.41%, H content of 3.28%, and heating value of 32.86 MJ/kg.
Keywords: adhesive content, charcoal briquette, pyrolysis, rubber wood waste, tapioca starch
References
Adekunle, J., Ibrahim, J., and Kucha, E. 2015. Proximate and Ultimate Analysis of Biocoal Briquette of Nigerian’s Ogboyaga and Okaba Sub-bituminous Coal. Brithis Journal of Applied Science and Technology, 7(1): 114-123.
Adrian, A., Sulaeman, R., dan Oktorini, Y. 2015. Karakteristik Wood Pellet dari Limbah Kayu Karet (Hevea brasiliensi Muell. Arg) Sebagai Alternatif Sumber Energi Terbarukan. Jom Faperta, 2(2): 1-6.
Akowuah, J. O., Kemausor, F dan Mitchual, S. J. 2012. Physico-Chemical Characteristics and Market Potential of Sawdust Charcoal Briquette. International Journal of Energy and Environmental Engineering, 3(1): 1-6.
Almu, M. A., Syahrul, dan Padang, Y. A. 2014. Analisa Nilai Kalor dan Laju Pembakaran pada Briket Campuran Biji Nyamplung (Calophyllm inophyllum) dan Abu Sekam Padi. Dinamika Teknik Mesin, 4(2): 117-122.
Anderson, J., Helwani, Z., dan Komalasari. 2017, Proses Densifikasi Pelepah Sawit Menggunakan Gliserol Sebagai Filler Menjadi Bahan Bakar Padat. Jom FTEKNIK, 4(1): 1-4.
Anita, M. F. 2019. Pembuatan Briket Pelepah Kelapa Sawit (Elaegis guenensis Jacq) dengan Menggunakan Perekat Biji Durian Sebagai Energi Baru Terbarukan. [Skripsi]. 71 hlm.
Basuki, H. W., Yuniarti., dan Fatriani. 2020. Analisia Fisik dan Kimia Briket Arang dari Campuran Tandan Kosong Aren (Arenga pinnata Merr) dan Cangkang Kemiri (Aleurites trisperma). Jurnal Sylva Scienteae, 3(4): 626-636.
BPS. 2020. Statistik Indonesia 2020. Badan Pusat Statistik: Jakarta, Indonesia.
Briyartendra, E. I dan Widayat, W. 2019. Pengaruh Ukuran Partikel dan Tekanan Kompaksi Terhadap Karakteristik Briket Kayu Jati. Jrnal Inovasi Mesin. 1(2): 14-22.
Chaney, J. O. 2010. Combustion Characteristics of Biomass Briquettes. [Thesis]. 224 hlm.
Chew, J. J., dan Doshi, V. 2011. Recent Advances in Biomass Pretreatment - Torrefaction Fundamentals and Technology. Renewable and Sustainable Energy Rev, 15(8): 4212-4222.
Direktur Jendral Bina Usaha Kehutanan. 2009. Rendemen Kayu Olahan Industri Primer Hasil Hutan Kayu (HHK). Kementerian Kehutanan. Jakarta. 4 hlm
Faizal, M., Andynapratiwi, I., dan Putri, P.D.A. 2014. Pengaruh Komposisi Arang dan Perekat Terhadap Kualitas Biobriket dari Kayu Karet. Teknik Kimia, 20(2): 36-44
Gandhi B, A. 2010. Pengaruh Variasi Jumlah Campuran Perekat Terhadap Karakteristik Briket Arang Tongkol Jagung. Profesional, 8(1): 1-12.
Gusti A, R. 2018. Pengaruh Variasi Sudut Tekuk dan Sistem Pengerollan Terhadap Kualitas Hasil Pengerollan Pipa Aluminium dengan Menggunakan Mesin Roll Pneumatic. [Skripsi]. 79 hlm
Haryanto, A., Hidayat, W., Hasanudin, U., Iryani, D. A., Kim, S., Lee, S., dan Yoo, J. 2021. Valorization of Indonesian Wood Wastes through Pyrolysis: A Review. Energies, 14(5): 1407.
Hidayat, W., Qi, Y., Jang, J. H., Febrianto, F., Lee, S. H., Chae, H. M., Kondo, T., and Kim, N. H. 2017. Carbonization Characteristics of Juvenile Woods from Some Tropical Trees Planted In Indonesia. Journal of the Faculty of Agriculture, Kyushu University, 62(1): 145-152.
Hidayat, W., Rani, I. T., Febryano, I. G., Iryani, D. A., Hasanudin, U., Lee, S., Kim, S., Yoo, J., dan Haryanto, A. 2020. Peningkatan Kualitas Pelet Tandan Kosong Kelapa Sawit Melalui Torefaksi Menggunakan Reaktor Counter-Flow Multi Baffle (COMB). Jurnal Rekayasa Proses, 14(2):169-181.
Hidayat, W., Riniarti, M., Prasetia, H., Niswati, N., Hasanudin, U., Banuwa, I. S., Yoo, J., Kim, S., Lee, S. 2021. Characteristics of Biochar Produced from the Harvesting Wastes of Meranti (Shorea sp.) and Oil Palm (Elaeis guineensis) Empty Fruit Bunches. IOP Conference Series: Earth and Environmental Science, 749: 012040
Iryani, D. A., Haryanto, A., Hidayat, W., Amrul, Telaumbanua, M., Hasanudin, U., Lee, S. H. 2019. Torrefaction Upgrading of Palm Oil Empty Fruit Bunches Biomass Pellets for Gasification Feedstock by Using COMB (Counter Flow Multi-Baffle) Reactor. 7th TAE (Trend in Agricultural Engineering). 212-2017.
Isa, I., Lukum, H., dan Arif, I. H. 2012. Briket Arang dan Arang Aktif dari Limbah Tongkol Jagung. Laporan Penelitian. 50 hlm.
Kahariayadi, A., Setyawati, D., Nurhaida., Diba, F., dan Roslinda, E. 2015. Kualitas Arang Briket Berdasarkan Persentase Aranng Batang Kelapa Sawit (Elaeis guineensis Jacq) dan Arang Kayu Laban (Vitex pubescens Vahl). Jurnal Hutan Lestari, 3:561-568.
Kimutai, S. K dan Kimutai, I. K. 2019. Investigation of Physical and Combustion Properties of Briquette from Cashew Nut Shell and Cassava Binder. International Journal of Education and Research, 7(11): 15-26.
Kwon, G, J., Kim, A, R., Lee, H, S., Lee, S, H., Hidayat, W., Febrianto, F., dan Kim, N, H. 2018. Characteristics of White Charcoal Produced from the Charcoal Kiln for Thermotherapy. Journal of the Korean Wood Science and Technology, 46(5): 527-540.
Lukmuang, R., Dasaard, C., Chantawong, P., dan Ngamrungroj, D. Material Ratio Analysis of Charcoal Briquettes from Dendrocalamus Asper Backer Bamboo. The International Conference on Materials Research and Innovation. 1-4.
Maryono, S dan Rahmawati. 2013. Preparation and Quality Analysis of Coconut Shell Charcoal Briquette Observed by Starch Concentration. Journal Chemical, 14(1):74-83.
Matangaran, J. R., dan Anggoro, R. 2012. Limbah Pemanenan Jati di Banyuwangi Jawa Timur. Jurnal Perennial, 8(2): 88-92.
Mawardi, I., Nurdin., Ariefin., Usman, R, dan Abdel. 2019. Peningkatan Karakteristik Biopellet Kayu Kelapa Sawit Sebagai Energi Alternatif. Prosiding Seminar Nasional Politeknik Negeri Lhokseumawe. Aceh Utara, 3 Oktober 2019. 3(1): A230-A234
Moeksin, R., Pratama, A. A., dan Tyani, D. R. 2017. Pembuatan Briket Bioarang dari Campuran Limbah Tempurung Kelapa Sawit dan Cangkang Biji Karet. Jurnal Teknik Kimia, 23(3): 146-156.
Nasrul, Z. A., Maulinda, L., Darma, F., dan Meriatna. 2020. Pengaruh Komposisi Briket Biomassa Kulit Jagung terhadap Karakteristik Briket. Jurnal Teknologi Kimia Unimal, 9(2): 35-42.
Nasution, Z. A dan Rambe, S. M. 2013. Karakteristik dan Identifikasi Gugus Fungsi dari Karbon Cangkang Kelapa Sawit dengan Metode Methano-Pyrolisis. Jurnal Dinamika Penelitian Industri, 24(2):108-113.
Nhuchhen, D. R., Afzal, M. T. 2017. HHV Predicting Correlations for Torrefied Biomass Using Proximate And Ultimate Analyses. Bioengineering, 4(7): 1- 15.
Ningsih, E., Mirzayanti, Y. W., Himawan, H. S., dan Indriani, M. 2016. Pengaruh Jenis Perekat pada Briket dari Kulit Nuah Bintaro Terhadap Waktu Bakar. Prosiding Seminar Nasional Teknik Kimia “Kejuangan†Pengembangan Teknologi Kimia untuk Pengolahan Sumber Daya Alam Indonesia Yogyakarta. Program Studi Teknik Kimia, FTI, UPN “Veteran†Yogyakarta. 1-8.
Pane, J. P., Junary, E., dan Herlina, N. 2015. Pengaruh Konsentrasi Perekat Tepung Tapioka dan Penambahan Kapur Pembuatan Briket Arang Berbahan Baku Pelepah Aren (Arenga pinnata). Jurnal Teknik Kimia USU, 492: 32-38.
Park, S. H., Jang, J. H., Qi, Y., Hidayat, W., Hwang, W., Febrianto, F., and Kim, N. H. 2018. Anatomical and Physical Properties of Indonesian Bamboos Carbonized at Different Temperatures. Journal of the Korean Wood Science and Technology, 46(6): 9-18.
Qi, Y., Jang, J. H., Hidayat, W., Lee, A. H., Lee, S. H., Chae, H. M., and Kim, N. H. 2016. Carbonization of Reaction Wood from paulownia tomentosa and pinus densiflora Branch Woods. Wood Science and Technology, 50(5): 973–987.
Rahmadani., Hamzah, F., dan Hamzah, F.H. 2017. Manufacture Oil Palm’s Leaves (Elaeis guineensis Jacq.) Charcoal Briquet With Sago Starch Adhesive (Metroxylon sago Rott.). JOM Faperta UR, 4(1): 1-11.
Raju, M. 2016. Karakterisasi Arang dan Gas-gas Hasil Pirolisis Limbah Kelapa Sawit. Jurnal Keteknikan Pertanian, 4(2): 153-160.
Rani, I.T., Hidayat, W., Febryano, I.G.,Iryani, D.A., dan Haryanto, A., dan Hasanudin, U. 2020. Pengaruh Torefaksi Terhadap Sifat Kimia Pelet Tandan Kosong Kelapa Sawit. Jurnal Teknik Pertanian Lampung, 9(1): 63-70.
Ridjayanti, S.M., Bazenet, R.A., Hidayat, W., Banuwa, I.S., dan Riniarti, M. 2021. Pengaruh Variasi Perekat Tapioka terhadap Karakteristik Briket Arang Limbah Kayu Sengon (Falcataria moluccana). Jurnal Perennial, 17(1): 5-10.
Riniarti, M., Hidayat, W., Prasetia, H., Niswati, N., Hasanudin, U., Banuwa, I. S., Yoo, J., Kim, S., Lee, S. 2021. Using Two Dosages of Biochar from Shorea to Improve the Growth of Paraserianthes falcataria Seedlings. IOP Conference Series: Earth and Environmental Science. 749: 012049.
Rubiyanti, T., Hidayat, W., Febryano, I. G., dan Bakri, S. 2019. Karakteristik Pelet Kayu Karet (Hevea brasiliensis) Hasil Torefaksi dengan Menggunakan Reaktor Counter-Flow Multi Baffle (COMB). Jurnal Sylva Lestari, 7(3): 321-331.
Shobar, S., Sribudiani, E., dan Somadona, S. 2020. Karakteristik Briket Arang dari Limbah Kulit Buah Pinang dengan Berbagai Komposisi Jenis Perekat. Jurnal Sylva Lestari, 8(2): 189-196.
Smith, H., dan Idrus, S. 2017. Pengaruh Penggunaan Perekat Sagu dan Tapioka terhadap Karakteristik Briket dari Biomassa Limbah Penyulingan Minyak Kayu Putih di Maluku. Majalah Biam, 13(2): 21-32.
Standar Nasional Indonesia. 2000. SNI Briket Arang Kayu SNI 01-6235- 2000.Badan Standarisasi Nasional – BSN.
Sukarman, Anwar, C., Rahdiana, N., Khoirudin., dan Ramadhan, A. I. 2020. Analisis Pengaruh Radius Dies Terhadap Springback Logam Lembaran Stainless-Steel pada Proses Bending Hidrolik V-DIE. Jurnal Teknologi, 12(2): 123-132.
Sulistio, Y., Febryano, I.G., Hasanudin, U., Yoo, J., Kim, S., Lee, S., dan Hidayat, W. 2020. Pengaruh Torefaksi dengan Reaktor Counter-Flow Multi Baffle (COMB) dan Electric Furnace terhadap Pelet Kayu Jabon (Anthocephalus cadamba). Jurnal Sylva Lestari, 8(1): 65-76.
Suryani, E., Farid, M., dan Mayub, A. 2019. Implementasi Karakteristik Nilai Kalor Briket Campuran Limbah Kulit Durian dan Tempurung Kelapa pada Pembelajaran Kulit Durian dan Tempurung Kelapa pada Pembelajaran Suhu dan Kalor di SMP N 15 Kota Bengkulu. Journal of Science Education, 3(3):146-153.
Susanto, A dan Yanto, T. 2013. Pembuatan Briket Bioarang dari Cangkang dan Tandan Kosong Kelapa Sawit. Jurnal Teknologi Hasil Pertanian, 6(2): 68-81.
Tarigan, A.A.L.B., Riniarti, M., Prasetia, H., Hidayat, W., Niswati, N., Banuwa, I.S., dan Hasanudin, U. 2021. Pengaruh Biochar pada Simbiosis Rhizobium dan Akar Sengon Laut (Paraserianthes falcataria) dalam Media Tanam. Journal of People, Forest and Environment, 1(1): 11-20.
Tippayawong, K.Y., Santiteerakul, S., Ramingwong, S., dan Tippayawong. 2019. Cost Analysis of Community Scale Smokeless Charcoal Briquette Production from Agricultural and Forest Residues. Energy Procedia: 310-316.
Woelan, S., Siagian, N., Sayurandi., dan Pasaribu, S.A. 2012. Potensi Kayu Karet Hasil Peremajaan di Tingkat Perusahaan Perkebunan. Warta Perkebunan, 31(2): 75-84.
Yulianto, T., Febryano, I. G., Iryani, D.A., Haryanto, A., Hasanudin, U., dan Hidayat, W. 2020. Perubahan Sifat Fisis Pelet Tandan Kosong Kelapa Sawit Hasil Torefaksi. Jurnal Teknik Pertanian Lampung, 9(2): 104-111.
Downloads
Published
Issue
Section
License
- Authors who publish with this journal agree to the following terms:
- Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution-ShareAlike 4.0 International Lice that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
- Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
- Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).
Jurnal Teknik Pertanian Lampung
JTEPL is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.